Polymer waterproof materials are one of the chemical building materials, with environmental protection and excellent physical and chemical properties, widely used in residential buildings, industrial and commercial buildings, water conservancy projects and underground engineering and other building waterproof engineering. Beixin waterproof polymer waterproof roll is made of synthetic rubber, synthetic resin or the blend of the two as the base material, adding the right amount of chemical additives and filler, using the processing technology of rubber or plastics such as mixing, extrusion or calendering can be rolled into sheets of waterproof material.
Polymer waterproof material series products
Thermoplastic Polyolefin (TPO) Waterproof Membrane
Polymer waterproof material series products
★ Product Description download
1.2 1.5 1.8 2.0
Thickness /mm:
TPO waterproof membrane classification:HHomogeneous type/YWG-610YWG-610 Thermoplastic Polyolefin (TPO) Waterproof Membrane:With fiber backing/YWG-610 Thermoplastic Polyolefin (TPO) Waterproof Membrane; In-fabric enhancement/YWG-610 Thermoplastic Polyolefin (TPO) Waterproof Membrane
Product Classification:
————
The product is made of thermoplastic polyolefin synthetic resin (TPO) as the base material and adopts advanced processing technology to make flake polymer waterproof material. TPO membrane is made of EPDM rubber for weathering and aging resistance and polypropylene for weld ability. In addition, it has the advantages of chemical corrosion resistance, high and low temperature resistance, and good dimensional stability.
PRODUCT INTRODUCTION
Cold sticking method:The use of special supporting glue, the membrane paste on the base of the construction method, divided into full bonding or local bonding method. Finally, the membrane lap edge welding can be compacted.
Mechanical fixation method:The construction method of connecting the membrane with the base by mechanical fasteners. The membrane lap edge welding can be compact.
Construction Method
Machinery welding joint:The use of climbing welder for welding, suitable for large area construction, quick construction.
Hand welding joint:Hand-held welder is used for welding, suitable for detail construction and small area construction.Manual welding can be divided into three steps: "spot welding", "pre-welding" and "solid welding" to ensure the welding effect.
Spot welding: used to fix the membrane and prevent the membrane from shifting. When spot welding, gently press the membrane surface with the tip of the gun.
Pre-welding: it can seal, prevent hot air from blowing away, and can't reach the welding temperature.
Solid welding: weld the two rolls of membrane into a whole.
Construction Method
CONSTRUCTION METHOD
Through
Resistance to root puncture
≥80 Membrane damaged
Joint stripping strength
Retention rate after heat aging treatment/%
Welding:≥3.0 Membrane damaged
Bonding:≥1.5
Joint stripping strength
No processing/(N/mm)
Mould proof level:level0 level1
Mold corrosion resistance
Planting roof application performance and requirements
(Note: static load resistance is only required for membrane used for press-laying roof)
≤4.0
Water absorption
(70℃,168h)/%
-(H);≥250(L);
450(P)
Trapezoidal tearing Strength/(N)
H≥60(H);-(L);
-(P)
Right-angled tearing strength/(N/mm)
≥4.0 Membrane damaged(H);≥3.0(L);≥3.0(P)
Joint stripping strength/(N/mm)
-(H); -(L);
20Kg impermeable(P)
Static load resistance
0.5kg·m,impermeable
Impact resistance
0.3,2h impermeable
Unpermeability/MPa
-40,no crack
Cold bending/℃
≤2.0(H);≤1.0(L);
≤0.5(P)
Heat treatment scale change rate/%
Break elongation/%
≥500(H);
≥250(L);-(P)
Tensile property
Tensile strength/MPa
≥12.0(H); -(L);-(P)
Tensile property
Maximum tension/(N/cm)
-(H);≥200(L);≥250(P)
Tensile property
-(H);-(L);≥0.40(P)
Thickness of resin layer above intermediate substrate/mm
Physical Index
GB 27789-2011 thermoplastic polyolefin (TPO) waterproof membrane;GB/ t35468-2017 root puncture resistant waterproof membrane for planting roof。
Executive Standard
Elongation at maximum tension/%
-(H); -(L);≥15(P)
Tensile property
It is mainly applied to the roofing, underground and other waterproof works of industrial and civil buildings.
APPLICATION FIELD
From Monday to Saturday at 8:00am -18:00pm
Email :wugang@bnbm.com.cn
Address: South of Xingyou Street, West of Jinger Road, Xinglongtai District, Panjin City, Liaoning Province, China
400-600-0427
Contact us
Hydro power
Municipal building
Commercial building
Civil building
Bridge, tunnels and roads
Overseas engineering
Rail roads and subways
Major projects
Classical engineering cases
Waterproof coating ranges
Excellent and Secure Waterproofing System Ranges
Polymer ranges of waterproof materials
Self adhering ranges of modified asphalt waterproof membrane
Hot-torched ranges of modified asphalt waterproof membrane